Sliding Wear Study of Flame Sprayed Co-Base Powder Coatings
Indexed in
Technology and Engineering
ARTICLE-FACTOR
1.3
Article Basics Score: 3
Article Transparency Score: 3
Article Operation Score: 2
Article Articles Score: 3
Article Accessibility Score: 3
SUBMIT PAPER ASK QUESTION
International Category Code (ICC):
ICC-1802
Publisher: Lifescience Global Inc.
International Journal Address (IAA):
IAA.ZONE/2369108593355
eISSN
:
2369 - 3355
VALID
ISSN Validator
Abstract
Commercially available Co-base powder was modified with the addition of 10 wt. percentage WC which was further modified with 5 and 10 wt. percentage CrC addition in order to obtain three coatings namely Co+10 wt. percentage WC, Co+10 wt. percentage WC+5 wt. percentage CrC and Co+10 wt. percentage WC+10 wt. percentage CrC. The coatings were deposited by flame spraying process. The microstructure of these coatings mainly showed eutectic containing Co with almost same amount in three coatings. Other phases such as W dominated and Cr dominated carbides were also observed. The 10 wt. percentage CrC coating showed the highest Vickers hardness and lowest wear rate. The coefficient of friction was also observed low in the 10 wt. percentage CrC coating as compared with other coatings.